Nucleosil® (Macherey & Nagel)
Pore diameter
50, 100, 120, 300, 500, 1000, 4000 A°
Pore volume
0.8, 1.0, 0.65, 0.7 ml/g
Surface area
450, 350, 200, 100, 35, 25, 10 m²/g
Specifications
| Particle Sizes | 3 µm, 5 µm, 7 µm, 10 µm, 12 µm |
|---|---|
| Phases/Modifications | / CN, Nitrile |
| Pore Size | Surface Area |
|---|---|
| Å | m²/g |
| 50 Å | 450 m²/g |
| 100 Å | 350 m²/g |
| 120 Å | 200 m²/g |
| 300 Å | 100 m²/g |
| 500 Å | 35 m²/g |
| 1000 Å | 25 m²/g |
| 4000 Å | 10 m²/g |
Products
| Name | Particle Sizes | Carbon Load | Pore Size |
|---|---|---|---|
| Nucleosil 50 Si | 5 – 10 µm | 0 % | 50 Å |
| Nucleosil 50 C8-ec | 5 µm | 0 % | 50 Å |
| Nucleosil 50 C18-ec | 5 µm | 0 % | 50 Å |
| Nucleosil 100 Si | 3 – 7 µm | 0 % | 100 Å |
| Nucleosil 100 C2 | 7 µm | 3 % | 100 Å |
| Nucleosil 100 C8 | 5 – 10 µm | 9 % | 100 Å |
| Nucleosil 100 C8-ec | 5 µm | 9 % | 100 Å |
| Nucleosil 100 C18 | 3 – 12 µm | 15 % | 100 Å |
| Nucleosil 100 C18-AB | 5 µm | 25 % | 100 Å |
| Nucleosil 100 C18-HD | 5 µm | 0 % | 100 Å |
| Nucleosil 100 Phenyl (C6H5) | 7 µm | 8 % | 100 Å |
| Nucleosil 100 Phenyl-ec (C6H5-ec) | 5 µm | 0 % | 100 Å |
| Nucleosil 100 CN | 5 – 10 µm | 5 % | 100 Å |
| Nucleosil 100 NH2 | 5 – 10 µm | 3 % | 100 Å |
| Nucleosil 100 N02 | 5 – 10 µm | 0 % | 100 Å |
| Nucleosil 100 N(CH3)2 | 5 – 10 µm | 0 % | 100 Å |
| Nucleosil 100 SA | 5 – 10 µm | 6 % | 100 Å |
| Nucleosil 100 SB | 5 – 10 µm | 10 % | 100 Å |
| Nucleosil 100-OH (Diol) | 7 µm | 5 % | 100 Å |
| Nucleosil Chiral-2 | 5 µm | 0 % | Å |
| Nucleosil Delta-S | 5 – 5 µm | 0 % | Å |
| Nucleosil 120 Si | 3 – 10 µm | 0 % | 120 Å |
| Nucleosil 120 C4 | 5 µm | 4 % | 120 Å |
| Nucleosil 120 C8 | 3 – 10 µm | 6 % | 120 Å |
| Nucleosil 120 C18 | 3 – 10 µm | 11 % | 120 Å |
| Nucleosil 120 C6H5 (Phenyl) | 7 µm | 6 % | 120 Å |
| Nucleosil 120 CN | 7 µm | 5 % | 120 Å |
| Nucleosil 120 NH2 | 7 µm | 0 % | 120 Å |
| Nucleosil 300 Si | 5 – 10 µm | 0 % | 300 Å |
| Nucleosil 300 C4 | 5 – 10 µm | 0 % | 300 Å |
| Nucleosil 300 C8 | 5 – 10 µm | 0 % | 300 Å |
| Nucleosil 300 C18 | 5 – 10 µm | 0 % | 300 Å |
| Nucleosil 300 C6H5 (Phenyl) | 7 µm | 0 % | 300 Å |
| Nucleosil 300 OH (Diol) | 7 µm | 0 % | 300 Å |
| Nucleosil 300 CN | 7 µm | 0 % | 300 Å |
| Nucleosil 300 NH2 | 7 µm | 0 % | 300 Å |
| Nucleosil 500 Si | 5 – 10 µm | 0 % | 500 Å |
| Nucleosil 500 C4 | 7 µm | 0 % | 500 Å |
| Nucleosil 500 C8 | 7 µm | 0 % | 500 Å |
| Nucleosil 500 C18 | 7 µm | 0 % | 500 Å |
| Nucleosil 500 C6H5 (Phenyl) | 7 µm | 0 % | 500 Å |
| Nucleosil 500 OH (Diol) | 7 µm | 0 % | 500 Å |
| Nucleosil 500 CN | 7 µm | 0 % | 500 Å |
| Nucleosil 1000 Si | 5 – 10 µm | 0 % | 1000 Å |
| Nucleosil 1000 C4 | 7 µm | 0 % | 1000 Å |
| Nucleosil 1000 C18 | 7 µm | 0 % | 1000 Å |
| Nucleosil 1000 C6H5 (Phenyl) | 7 µm | 0 % | 1000 Å |
| Nucleosil 1000 OH (Diol) | 7 µm | 0 % | 1000 Å |
| Nucleosil 4000 OH | 7 µm | 0 % | 4000 Å |
| Nucleosil 4000 C4 | 7 µm | 0 % | 4000 Å |